Bu kaydın yasal hükümlere uygun olmadığını düşünüyorsanız lütfen sayfa sonundaki Hata Bildir bağlantısını takip ederek bildirimde bulununuz. Kayıtlar ilgili üniversite yöneticileri tarafından eklenmektedir. Nadiren de olsa kayıtlarla ilgili hatalar oluşabilmektedir. MİTOS internet üzerindeki herhangi bir ödev sitesi değildir!

Improvement of Mechanical and Physical Properties of Polyurethane Elastomer/Jute Fiber Eco-Composites By Applying Proper Treatments To Fiber Surfaces

Oluşturulma Tarihi: 01-08-2017

Niteleme Bilgileri

Tür: Tez

Alt Tür: Yüksek Lisans Tezi

Yayınlanma Durumu: Yayınlanmamış

Dosya Biçimi: PDF

Dil: İngilizce

Konu(lar): Kimyasal teknoloji, Kimya mühendisliği,

Yazar(lar): Salem, Tuffaha Fathe Salem (Yazar), Tirkeş, Seha (Yazar),

Emeği Geçen(ler):

Anahtar Kelimeler

Polyurethane Elastomer, Jute Fiber, Surface Treatment, Eco-composite.


Özet

In this study, chopped jute fiber (JF) samples were surface treated by alkaline (Na),silane(Si) and eco-grade epoxy resin(EP). Surface characteristics of jute fibers wereexamined by FTIR and EDX analysis. JF filled polyurethane elastomer (TPU)composites were prepared via melt compounding. The effect of surface modificationsof JF on mechanical, damping, melt-flow and morphological properties of TPUbased eco-composites were investigated by performing tensile and Shore hardnesstests, dynamic mechanical analysis (DMA), melt flow index (MFI) test and scanningelectron microscopy (SEM) techniques, respectively.Mechanical test results showed that silane and epoxy treated JF improved the tensilestrength and tensile modulus of unfilled TPU. Elongation at break of TPU decreaseddrastically with all kind of JF inclusions. All of the surface treatments resultedincrease in hardness value of TPU. Similarly with mechanical test results, Si-JF andEP-JF containing composites showed enhancement on storage modulus. Glasstransition temperature (Tg) of TPU rised up to higher temperatures after JF additions.Inclusions of JF caused increase for MFI value of neat TPU. Silane and epoxy treatedJFs displayed homogeneous dispersion into TPU and their surface were covered bypolymer phase according to SEM microphotographs.


İçindekiler



Açıklamalar



Haklar



Notlar



Kaynakça


Atıf Yapanlar

Gözat Sayfasına Dön

 

Sosyal Medya ve Araçlar

İstatistikler

  • Kayıt
    • Bu ay: 0
    • Toplam: 2441
  • Online
    • Ziyaretçi: 66
    • Üye: 0
    • Toplam: 66

Detaylı İstatistikler